Principle: Colored Nylon 6 Yarn dye and melt are fully mixed during polymerization, and colored yarn is obtained by spinning.
Advantages: Colored Polymaide6 Yarn does not dye after weaving, does not discharge dyeing sewage, saves water, saves energy, and is green and environmentally friendly. It realizes the true meaning of green yarn in situ polymerization, has high color fastness, uniform color, no color difference between batches, and improves post-treatment efficiency.
Product features
1. T 1. More environmental protection
When Pa6 Black Chips is polymerized in situ, the polymerization will turn black to avoid energy consumption and environmental pollution in the process of masterbatch production.
Reduce the harm of dust to employees during masterbatch production
2. No change in equipment
Since the chip is an In situ Pa6 Black Chips, it can be directly used to reduce the input of the main syringe and other devices. At the same time, it is also the world's first large-scale production of in-situ polymerization of black profiles.
3. Longer component life
Using nanoscale pigments can achieve longer component cycles and higher throughput. Generally speaking, the masterbatch spinning component needs to be replaced within 15-25 days, but the black profile polymerized in situ can be used for 40-60 days, and the pressure of the component is basically unchanged
2.4 False twist friction plate has little damage and no damage to the knitting needle
Nanometer pigment, more finely dispersed, more uniform, and smoother surface. Reduce friction plate damage and knitting needle wear, and reduce crochet phenomenon
3.5. More uniform color, no color difference and higher color fastness
In the spinning process, the color difference and low color fastness caused by uneven masterbatch addition are avoided, so that the color uniformity is better and the color is blue. The color fastness reaches Grade 5 (gray card), the sun resistance, acid and alkali resistance, and the washing fastness reaches Grade 4.5 (gray card)
6. Anti static
Its antistatic performance is better than that of white yarn dyeing
HIGHSUN Group, a world famous enterprise, has been using products of the following specifications, and other varieties are being trial spun, with better results
FDY 40 days/12 days
POY 50D/34F
Hoy 45D/12F