YARN USE IN-SITU BRIGHT PA6 black film

The first batch of yarns produced in the world use Pa6 Black Chips.
Principle: dye and melt are fully mixed during polymerization of In situ Pa6 Black Chips, and colored yarn is obtained by spinning.
Advantages: Yarn Use Pa6 Black Chips will not dye after weaving and will not discharge dyeing sewage. It will save water, energy and environmental protection. It will realize real in-situ polymerization of Yarn Use Pa6 Black Chips, with high color fastness, uniform color, no color difference between batches, and improved post-processing efficiency.
Product features
1. T 1. More environmental protection
When Nylon 6 Granule is polymerized in situ, the polymerization will turn black to avoid energy consumption and environmental pollution in the master batch production process.
Reduce dust damage to employees during masterbatch production
2. No change in equipment
Because the chip is black, it can be directly used to reduce the input of the main syringe and other devices. At the same time, it is also the first company in the world to mass produce in-situ polymerized black profiles.
3. Longer component life
Using nanoscale pigments can achieve longer component cycles and higher throughput. Generally speaking, the masterbatch spinning components need to be replaced within 15-25 days, but the black profiled materials polymerized in situ can be used for 40-60 days, and the pressure of the components is basically unchanged
2.4 False twist friction plate has little damage and no damage to knitting needle
Nano pigment, more finely dispersed, more uniform, and more smooth surface. Reduce friction plate damage and knitting needle wear, and reduce crochet phenomenon
3.5. More uniform color, no color difference and higher color fastness
In the spinning process, the color difference and low color fastness caused by uneven masterbatch addition are avoided, so that the color uniformity is better and the color is blue. The color fastness shall reach Grade 5 (gray card), the sun resistance, acid and alkali resistance, and the washing fastness shall reach Grade 4.5 (gray card)
6. Anti static
Its antistatic performance is better than that of white yarn dyeing
HIGHSUN Group, a world famous enterprise, has been using products of the following specifications, and other varieties are being trial spun with good results

FDY 40D/12F 

POY 50D/34F 

HOY 45D/12F